nanocomposite; Nd 2Fe 14 B; melt spun ribbons

作者:白飞明,姜忠良,陈秀云,马春来,朱静
关键词:nanocomposite; Nd  2Fe    14  B; melt  spun ribbons; interaction; rare earths
单位:School of Materials magnetic materials
http://www.999magnet.com Science & Engineering, Tsinghua University,School of Materials Science & Engineering, Tsinghua University,School of Materials Science & Engineering, Tsinghua University,School of Materials Science & Engineering, Tsinghua University,School of Materials Science & Engineering, Tsinghua University Beijing 100084,China









,Beijing 100084,China









,Beijing 100084,China









,Beijing 100084,China









,Beijing 100084,China
摘要:Effect of multiple alloying elements (Ga, Nb, Zr, Hf and Pr) on microstructure and magnetic properties of nanocomposite Nd    9-  x    Pr    x  Fe    86.5-  y-z-m-n    Ga    y  Nb    z  Zr    m  Hf    n  B    4.5   (  x  =0, 2  25;   y, z, m, n  =0.5, 1.0) ribbons was investigated by a L    16  (2    15  ) orthogonal experiment. The results show that the addition of multiple alloying elements can effectively reduce the grain size of Nd  2Fe    14  B and α  Fe phases and promote amorphous phase to occur at low wheel speed. No inhomogeneous growth of grains was found in annealed ribbons, but a large amount of additives would results in irregularity of Nd  2Fe    14  B and α  Fe grains. On the other hand, addition of multiple alloying elements has complex effects on magnetic properties due to interactions between alloying elements. When the content of Nb is 0.5%, increasing the content of Pr and Ga and decreasing the content of Zr and Hf can improve the magnetic properties effectively. The optimum magnetic properties were obtained in Nd    2.25  Pr    6.75  Fe    84.5  Ga    1.5  Nb    0.5  B    4.5   ribbons spun at 15 m·s    -1   with   J    r=1.053 T,       i  H    c=530.9   kA·m    -1    ,(  BH  )    max  =124 kJ·m    -3  .